雜質含量不大于%

TaNbFeSiNiWMoTiNbOCHNTa1剩余——0.0050.0050.0020.010.010.0020.040.020.010.00150.01Ta2剩余——0.030.020.0050.040.030.0050.10.030.010.00150.01TaNb3剩余＜3.50.030.030.0050.040.030.005——0.030.010.00150.01TaNb20剩余17.0～23.00.030.030.0050.040.030.005——0.030.010.00150.01Ta2.5W剩余
0.0050.0050.0023.00.010.0020.040.020.010.00150.01Ta10W剩余
0.0050.0050.002110.010.0020.040.020.010.00150.01

用戶如有特殊要求，雙方具體商定公差范圍：

直徑, 英寸 (毫米)	公差, +/-英寸 (毫米)
0.010~0.020 excl (0.254~0.508)	0.0005 (0.013)
0.020~0.030 excl (0.508~0.762)	0.00075 (0.019)
0.030~0.060 excl (0.762~1.524)	0.001 (0.025)
0.060~0.090 excl (1.524~2.286)	0.0015 ( 0.038)
0.090~0.125 excl (2.286~3.175)	0.002 (0.051)
0.125~0.187 excl (3.175~4.750)	0.003 (0.076)
0.187~0.375 excl (4.750~9.525)	0.004 (0.102)
0.375~0.500 excl (9.525~12.70)	0.005 (0.127)
0.500~0.625 excl (12.70~15.88)	0.007 (0.178)
0.625~0.750 excl (15.88~19.05)	0.008 (0.203)
0.750~1.000 excl (19.05~25.40)	0.010 (0.254)
1.000~1.500 excl (25.40~38.10)	0.015 (0.381)
1.500~2.000 excl (38.10~50.80)	0.020 (0.508)
2.000~2.500 excl (50.80~63.50)	0.030 (0.762)

機械性能（退火態）

棒材,直徑 0.125英寸(3.18毫米)~2.5" (63.5毫米)
牌號	極限抗拉強度min，磅/英寸2（兆帕）	屈服強度min，磅/英寸2（兆帕）	伸長率，min% （1英寸標距）
RO5200/RO5400	25000 (172)	15000 (103)	25
RO5252	40000 (276)	28000 (193)	20
RO5255	70000 (482)	55000 (379)	20
RO5240	40000 (276)	28000 (193)	25
絲材, 直徑, 英寸 (毫米)
牌號	直徑,英寸 (毫米)	極限抗拉強度min，磅/英寸2（兆帕）	伸長率，min%
RO5200/RO5400	0.010(0.254)~0.0149(0.379)	35000 (241)	10
	0.015(0.381)~0.0249(0.633)	35000 (241)	15
	0.025(0.635)~0.124(3.14)	30000 (207)	20
RO5252	0.010(0.254)~0.0149(0.379)	40000 (276)	5
	0.015(0.381)~0.0249(0.633)	40000 (276)	10
	0.025(0.635)~0.124(3.14)	40000 (276)	15
RO5255	0.010(0.254)~0.0149(0.379)	70000 (482)	5
	0.015(0.381)~0.0249(0.633)	70000 (482)	10
	0.025(0.635)~0.124(3.14)	70000 (482)	15
RO5240	0.010(0.254)~0.0149(0.379)	35000 (241)	10
	0.015(0.381)~0.0249(0.633)	35000 (241)	15
	0.025(0.635)~0.124(3.14)	35000 (241)	20